分別由樹脂(A)劑及硬化(B)劑所組成,具有不易燃特性。GigaBond 可以在短時間內膠合工件,硬化後立即上機開始加工,後續製程脫膠部分,在溫熱水中做分離作業即可。

Application

This product is specially applied to Semiconductor, Crystal, Porcelain, and Magnetic material ingot/block cutting.


Characteristics

• Excellent adhesive strength
• Quick hardening
• Easy to be debonded by hot water without using solvent or oven
• Easy to be blended (Weight Ratio A : B = 2 : 1)
• Good for large area mounting
• Non-flammability, no disgusting smell
• Customization is available upon request

Specification

GigaBond V1 V7
Viscosity cps (25°C)C) A B A B
165000 42000 25000 25000
± 15000 ± 7000 ± 5000 ± 5000
Appearance Rust White Rust White
Gel Time 3 ~ 5 (min) 5 ~ 8 (min)
Bond Strength After 0.5 Hours After 2 Hours
80 (kg/cm2) 100 (kg/cm2)
Max. Strength After 1 Hours After 6 Hours
100 (kg/cm2) 200 (kg/cm2)
Hardness 85 ± 5D 85 ± 5D
Mixing Ratio A : B = 1 : 1
Application Sapphire slicing Bonding Fixture
Debonding 70°C Water 200°C Oven
Debonding Time 10 min 30 min
Package A : 1KG / B:1KG

GigaBond V9
Viscosity cps (25°C) A B
150000 50000
± 15000 ± 10000
Appearance Rust White
Gel Time 3 ~ 7 (min)
Bond Strength After 2 Hours
100 (kg/cm2)
Max. Strength After 4 Hours
150 (kg/cm2)
Hardness 85 ± 5D
Mixing Ratio A : B = 1 : 1
Application Sapphire slicing Bonding Fixture
Debonding 70°C Water 200°C Oven
Debonding Time 20 min 30 min
Package A : 1KG / B:1KG
GigaBond S4 S7
Viscosity cps (25°C) A B A B
70000 16000 20000 3000
± 10000 ± 5000 ± 5000 ± 1000
Appearance Rust Milky Rust Milky
Gel Time 20 (min) 10 (min)
Bond Strength After 2 Hours After 2 Hours
200 (kg/cm2) 200 (kg/cm2)
Max. Strength After 6 Hours After 6 Hours
240 (kg/cm2) 240 (kg/cm2)
Hardness 85 ± 5D 85 ± 5D
Mixing Ratio A : B = 2 : 1
Application Silicon Slicing
Debonding 75°C Water
Debonding Time 15 min
Package A : 1KG / B:0.5KG